Abstract The Brazilian Buriti oil presents low extraction costs and relevant antioxidant properties. Thus, this work aimed to analyze Buriti oil biomaterial (BB), within its physicochemical properties, biocompatibility and cellular integration, with the purpose to the use as a growth matrix for Goat Wharton’s jelly mesenchymal stem cells. Biomaterials were produced from Buriti oil polymer (Mauritia flexuosa), for it’s characterization were performed Infrared Region Spectroscopy (FTIR) and Thermogravimetric Analysis (TG and DTG). The biointegration was analyzed by Scanning Electron Microscopy (SEM) and histological techniques. In order to investigate biocompatibility, MTT (3-(4,5-dimetil-2-tiazolil)-2,5-difenil-2H-tetrazólio) test and hemolytic activity tests were performed. The activation capacity of immune system cellswas measured by phagocytic capacity assay and nitric oxide synthesis . The BB presented an amorphous composition, with high thermal stability and high water expansion capacity, a surface with micro and macropores, and good adhesion of Wharton’s jelly mesenchymal stem cells (MSCWJ). We verified the absence of cytotoxicity and hemolytic activity, in addition, BB did not stimulate the activation of macrophages. Proving to be a safe material for direct cultivation and also for manufacturing of compounds used for in vivo applications.

Abstract To analyze the biocompatibility of the scaffold produced from a natural polymer derived from castor oil through hemolytic activity and antimicrobial activity, to enable the clinical application. Three in vitro tests were performed: Hemolytic activity test - Polymer partially dissolved in contact with blood agar; Hemolytic activity test in sheep's blood - Polymer extract with red blood cells solution; Antimicrobial activity test - Solid polymer in direct contact with E. Coli and S. Aureus. For hemolytic tests, none of the samples showed hemolysis. Negative hemolytic activity is a good indicator, as the maintenance of the blood clot in the area of the lesion is essential for the formation of new tissue. For the antimicrobial activity test, no significant activity was observed against the bacteria used. The polymer is not toxic to red blood cells, being viable for clinical application as a matrix for tissue regeneration.